碳环氧层板分层破坏断口的SEM分析
ANALYSIS OF DELAMINATION FRACTURE SURFACE OF MULTIDIRECTIONAL LAMINATES BY SEM
-
摘要: 用扫描电镜(SEM)研究了T300/648环氧多向展合板试样在不同受载条件下破坏的分层断裂表面;通过分析这些断裂表面的微观特征与断裂过程有关的一些信息,探计了分层机制和分层的典型断口形貌特征。Abstract: Delamination frcture surface for Graphite/Epoxy (T300/648) multidrectional under different loading conditions were studied by using a scanning electron microscopy.